China Has Broken The Production Of High Performance Carbon Fiber By Dry Spray Wet Process.

< p > China < a target= "_blank" href= "http://www.91se91.com/" > textile < /a > Industrial Federation organized in Lianyungang, Jiangsu, a technical appraisal meeting on technical achievements of "dry spray wet spinning GQ45 high performance carbon fiber engineering key technology and equipment R & D" organized by Zhongfu Shen Ying Carbon Fiber Co., Ltd., Lianyungang Eagle travel Textile Machinery Co., Ltd., China Composite Material Group Co., Ltd. and Jiangsu Olympic Refco Group Ltd.

< /p >

< p > by the expert group of the Chinese Academy of Engineering academician Sun Jinliang and Jiang Shicheng as the deputy director of the appraisal committee, the expert opinion group held that "the dry jet wet spinning GQ45 high performance carbon fiber engineering key technology and equipment development" project has pioneered the breakthrough in the international advanced dry jet wet spinning carbon fiber manufacturing technology, and developed a homogeneous polymerization system suitable for dry spray wet spinning, a low disturbance air level fiber forming system and a high-speed high power steam drafting system.

In terms of equipment, the project has independently developed and designed a fully mixed 60 cubic meter polymerizer, dry spray wet spinning fiber forming equipment, steam drafting equipment, a complete set of carbonization key equipment, and efficient solvent recovery and waste gas treatment system.

Based on the above key technology and equipment foundation, we have prepared carbon fiber products whose indexes all meet the national standard GQ4522 standard, and have been applied to many composite materials manufacturing enterprises, reflecting the good results.

The appraisal committee unanimously affirms that SYT45 products have reached the leading level in China and the advanced level of similar products in the world.

< /p >

< p > it is understood that Zhongfu divine eagle Carbon Fiber Co., Ltd. has a complete set of independent research and development of international mainstream technology dry spray wet spinning SYT45 equivalent to T700 grade high-performance carbon fiber precursor production line and carbonization production line, Zhongfu divine eagle has become the only enterprise in China and the world's third tackling dry spray wet spinning technology problems.

< /p >

< p > after 4 years of research and development, the company first broke the dry jet wet process technology of high-performance carbon fiber in China, and has now achieved large-scale production and bulk supply of the market.

< /p >

< p > SYT45 the tensile strength of high performance carbon fiber is above 4.5GPa and the modulus is 240GPa.

It is widely used in industrial, civil engineering, medical devices, sports products, military and aerospace fields.

The development of high performance carbon fiber SYT45 is not only an urgent need for modern national defense, but also a need for social and economic development of the country.

< /p >

< p > dry wet spinning is also called dry jet wet spinning.

Compared with wet spinning, dry wet spinning can produce high spinneret and high spinning speed. Dry wet spinning can form a dense thin layer in the air layer to prevent the formation of large pores, which is superior to wet spinning.

The fibers obtained by dry wet spinning process are relatively uniform in structure, small in core layer, high in strength and elasticity, nearly round in section structure, smooth in fiber surface, and few in fiber defects.

The fibers with high density and high bulk density can produce high performance carbon fibers, which are superior to those of wet spinning carbon fiber in the field of carbon fiber composites.

< /p >